The synthesis of Al2O3-coated and uncoated LiMn2O4 by solid-state method and fabrication of LiMn2O4/graphite battery were described. The structure and morphology of the powders were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The electrochemical and overcharge performances of Al2O3-coated and uncoated LiMn2O4 batteries were investigated and compared. The uncoated LiMn2O4 battery shows capacity loss of 16.5% after 200 cycles, and the coated LiMn2O4 battery only shows 12.5% after 200 cycles. The uncoated LiMn2O4 battery explodes and creates carbon, MnO, and Li2CO3 after 3C/10 V overcharged test, while the coated LiMn2O4 battery passes the test. The steadier structure, polarization of electrode and modified layer are responsible for the safety performance.