Anion-specific effects on the interaction forces between Al2O3 surfaces and dispersibility of Al2O3 colloids in electrolyte solutions

作者：Isobe Toshihiro^*; Nakagawa Yosuke; Hayashi Mikiro; Matsushita Sachiko; Nakajima Akira

来源：Colloids and Surfaces A: Physicochemical and Engineering Aspects , 2012, 396: 233-237.

DOI：10.1016/j.colsurfa.2011.12.072

• Atomic force microscopy
• Force curve
• DLVO theory

The interaction between an Al2O3 colloid and c-sapphire surface (0001) was investigated in an aqueous solution containing citrate ion, Cl-, NO3- or Br- using the colloidal probe method. The force curve measured in electrolyte solutions at pH = 4 showed a good agreement with the force curve predicted by the Derjaguin-Landau-Vervey-Overbeek theory at a long separation distance. The repulsive forces were observed at a shorter separation distance. The order of the strength of the repulsive force was citrate ion %26gt; Cl- %26gt; NO3- %26gt; Br-, corresponding to the Hofmeister series. All the force curves measured in aqueous solutions at pH = 10 were the same. This is caused by the cation (K+) selectively affecting surface interaction because the Al2O3 surface charged to negative at this pH. A particle size distribution measurement of the Al2O3 colloids in the 0.001-0.1 mol/L Cl- and Br- aqueous solution was carried out. The agglomerates of the Al2O3 colloids were observed in 0.1 mol/L Br- solutions. However, Al2O3 colloids were well dispersed in the other aqueous solutions, which are reflected by the force curve results. Jump-in was observed only in the force curve measured in the 0.1 mol/L Br- solutions and not in any other solutions.

• 出版日期2012-2-20