AlAsSb Avalanche Photodiodes with a Sub-mV/K Temperature Coefficient of Breakdown Voltage

作者：Xie Shiyu^*; Tan Chee Hing

来源：IEEE Journal of Quantum Electronics, 2011, 47(11): 1391-1395.

DOI：10.1109/JQE.2011.2165051

• AlAsSb
• avalanche breakdown
• avalanche photodiodes
• impact ionization
• temperature dependence of breakdown
• tunneling

The temperature dependence of dark current and avalanche gain were measured on AlAsSb p-i-n diodes with avalanche region widths of 80 and 230 nm. Measurements at temperatures ranging from 77 to 295 K showed that the dark current decreases rapidly with reducing temperature while avalanche gain exhibits a weak temperature dependence. No measurable band to band tunneling current was observed in the thinner diodes at an electric field of 1.07 MV/cm, corresponding to a bias of 95% of the breakdown voltage. Temperature coefficients of breakdown voltage of 0.95 and 1.47 mV/K were obtained from 80 and 230 nm diodes, respectively. These are significantly lower than a range of semiconductor materials with similar avalanche region widths. Our results demonstrated the potential of using thin AlAsSb avalanche regions to achieve low temperature coefficient of breakdown voltage without suffering from high band to band tunneling current.

• 出版日期2011-11