A Co-Fe alloy as alternative anode for solid oxide fuel cell

作者：Lu Z G; Zhu J H^*; Bi Z H; Lu X C

来源：Journal of Power Sources, 2008, 180(1): 172-175.

DOI：10.1016/j.jpowsour.2008.02.051

• solid oxide fuel cell
• ordering reaction
• alloy anode
• Co-Fe alloy

Anew type of Ni-free anode material based on Co0.5Fe0.5 + SDC (Sm0.2Ce0.8O1.9) was identified and evaluated using the La0.8Sr0.2Ga0.83Mg0.17O3 (LSGM) electrolyte-supported cells. The maximum power densities with humidified hydrogen at 800 degrees C using Au mesh and Pt mesh as anode current collector were 1.07 and 1.20 W cm(-2), respectively, which were comparable to that of the cell with the Ni + SDC anode. The cell with the new anode exhibited reasonable performance stability at 800 degrees C in hydrogen fuel; furthermore, no noticeable change in cell performance with the Co0.5Fe0.5 alloy anode was observed upon ordering reaction in the alloy to form the ordered alpha' phase at 650 degrees C.

• 出版日期2008-5-15