Fabrication and characterization of functionally graded nanoclay/glass fiber/epoxy hybrid nanocomposite laminates

作者：Megahed Ahmed Abou El Wafa^*; Megahed Mona

来源：Iranian Polymer Journal, 2017, 26(9): 673-680.

DOI：10.1007/s13726-017-0552-y

• Fabrication
• Function graded materials
• Mechanical properties
• Nanoclay
• Hybrid nanocomposite laminates

In this work, hardness, tensile, impact, bearing strength and water absorption tests were performed to study the mechanical properties of stepwise graded and non-graded hybrid nanocomposites. Three different stepwise graded nanocomposites and one non-graded (homogeneous) nanocomposite with the same geometry and total nanoclay content of 10 wt% were designed and prepared. Moreover, one neat glass fiber laminate was manufactured. The results of the tests indicated that addition of the graded and non-graded nanoclay improves hardness over neat glass fiber reinforcement. The maximum increase in hardness of about 53% over neat specimen is obtained for specimens that have the highest weight percentage (2 wt%) of the clay nanoparticles on its surface (S-specimen and the side of F-specimen that reinforced with 2 wt% nanoclay). The gradation process results in an increase in hardness of about 11% compared with non-graded (homogeneous) specimen. In addition, an improvement of 11.9% in strain-to-failure is achieved with specimen having greatest amount of nanoclay in the middle over neat glass fiber/epoxy composite. The other nanoclayfilled glass fiber composites have strain-to-failure close to neat glass fiber/epoxy. The addition of nanoclay reinforcement has insignificant effect on ultimate tensile strength, tensile modulus, water absorption, bearing strength and impact strength compared with neat glass fiber/epoxy.

• 出版日期2017-9