A novel dual phase membrane 40 wt% Nd0.6Sr0.4CoO3-δ-60 wt% Ce0.9Nd0.1O2-δ: design, synthesis and properties

作者：He, Yuan; Shi, Lei; Wu, Fan; Xie, Weiwei; Wang, Shu; Yan, Dong; Liu, Peijiang; Li, Man-Rong; Caro, Jurgen^*; Luo, Huixia^*

来源：Journal of Materials Chemistry A, 2018, 6(1): 84-92.

DOI：10.1039/c7ta07842k

• IMPROVED OXYGEN PERMEABILITY
• CO2 CAPTURE
• ELECTRONIC CONDUCTOR
• COMPOSITE MEMBRANES
• SURFACE EXCHANGE
• PERMEATION
• SEPARATION
• MICROSTRUCTURE
• DEPENDENCE
• STABILITY

Oxygen permeation, stability and chemical bonding characteristics of 40 wt% Nd0.6Sr0.4CoO3-delta-60 wt% Ce0.9Nd0.1O2-delta (40NSCO-60CNO) dual-phase composite membrane reactors were investigated. The 40NSCO-60CNO oxygen permeable membrane was prepared via an in situ one-pot one-step EDTA-citric acid method. The crystal structure of the 40NSCO-60CNO dual phase material was characterized by X-ray diffraction (XRD) and in situ XRD. The microstructure was investigated using transmission electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM) combined with energy-dispersive X-ray spectroscopy (EDXS) and electron energy-loss spectroscopy (EELS). The results show that the 40NSCO-60CNO composite represents a micro-scale mixture of only the two pure phases NSCO and CNO. The oxygen permeation fluxes through the 40NSCO-60CNO dual phase membrane were measured at elevated temperatures (900-1000 degrees C) with one side of it exposed to synthetic air and the other side to a flowing He gas stream. A stable oxygen permeation rate of 0.90 mL cm(-2) min(-1) was obtained with a 0.4 mm thick membrane under an air/He oxygen partial pressure gradient at 1000 degrees C. The 40NSCO-60CNO dual phase membrane with a thickness of 0.6 mm showed a stable oxygen flux of 0.55 mL cm(-2) min(-1) at 950 degrees C for 100 h under pure CO2 sweeping.

• 出版日期2018-1-7
• 单位中山大学