Aggregate Passivation: Lithium Hydroxide Aggregate Treatment to Suppress Alkali-Silica Reaction

作者：Hargis Craig W^*; Juenger Maria C G; Monteiro Paulo J M

来源：ACI Materials Journal, 2013, 110(5): 567-575.

• aggregate
• alkali-aggregate reaction
• durability
• expansion
• lithium compounds

Alkali-silica reaction (ASR) continues to be a concrete durability problem despite the many physical and chemical mitigation techniques known to successfully prevent it. The research presented herein tested a new method to limit ASR: aggregate passivation. A lithium silicate layer was created on reactive natural siliceous aggregate surfaces by treating the aggregates in a lithium hydroxide solution prior to use. A 4 M LiOH treatment was found to be superior to a 2 M LiOH treatment in producing a lithium silicate passivation layer and in reducing expansion due to ASR. The use of passivated aggregates greatly reduced expansion in accelerated mortar bar tests compared to nonpassivated aggregates and lithium-based admixtures.

• 出版日期2013-10