Size-Dependent Multiple-Scattering Effects of Mesoporous TiO2 Beads Distinguished by Optical Coherence Tomography

作者：Tsai Ling Hsuan; Yang Po Nien; Shih Yen Chen; Lin King Fu; Wu Chung Chih; Lin Hoang Yang^*

来源：IEEE Photonics Journal, 2017, 9(5): 6102210.

DOI：10.1109/JPHOT.2017.2734566

• Optical coherence tomography
• multiple scattering
• light scattering interaction

In this study, we propose a new analysis method using optical coherence tomography to further use the diffusive reflectance measurement to quantify the contribution of the size-dependent multiple-scattering effects of mesoporous TiO2 beads. The diffusive reflectance results from the complex interactions between light and the scattering particles, and influences the slopes of the associated depth-dependent A-scan profiles, which can be fitted based on the extended Huygens-Fresnel model to quantify the contribution ratio of the multiple-scattering effects to the single scattering effects. The mesoporous TiO2 beads with average diameter of 300 nm show higher contribution percentage of multiple-scattering effects inducing reflectivity enhancement in the longer wavelength region. The contribution ratio of multiple-scattering effects can be distinguished numerically, and is enhanced from 5% to 40% and then decreased to 20% for the bead diameters ranging from 20 to 300 nm and then to 500 nm, respectively. The calculated scattering coefficients are 13.5 +/- 0.6 mm(-1), 16.5 +/- 0.6 mm(-1), 20.2 +/- 0.6 mm(-1), and 18.5 +/- 0.6 mm(-1), respectively.

• 出版日期2017-10