Mechanical-Chemical Synthesis Ba0.77Sr0.23TiO3

作者：Kosanovic D^*; Obradovic N; Zivojinovic J; Filipovic S; Maricic A; Pavlovic V; Tang Y; Ristic M M

来源：Science of Sintering, 2012, 44(1): 47-55.

DOI：10.2298/SOS1201047K

• Mechanical activation
• Scanning electron microscopy
• Crystal structure
• Barium-strontium-titanate

Barium-Strontium-Titanate Ba0.77Sr0.23TiO3 was prepared from starting materials BaCO3, SrCO3 and TiO2 through solid-state reactions. Mixtures of these oxides are mechanically activated in a high-energy planetary ball mill at different time intervals from 0 to 120 minutes. In order to obtain information on phase composition, crystal structure was determent by X-ray diffraction. It was observed that after 80 minutes in process synthesis Ba0.77Sr0.23TiO3 started Thermal analyzes were performed in order to determine the characteristic temperatures of the processes that occur in the solid phase. Particle size distribution, together with electron microscopy scanning has given us very useful information about the morphology of the powder.

• 出版日期2012-4