In this study, a novel potential-triggered electroactive composite film consisting of mesoporous silica SBA-15, polyaniline (PANI), and polystyrenesulfonate (PSS) was fabricated in an aqueous electrolyte solution via a facile pulse potentiostatic method. The obtained composite film was characterized by Fourier transform infrared spectroscopy (FT-IR), thermogravimetric (TG) analysis, and scanning electron microscopy (SEM). The ion exchange properties were evaluated in a solution containing 0.1 M Pb(NO3)(2) by using an electrochemical quartz crystal microbalance (EQCM) as well as cyclic voltammetry (CV) method. It was found that the uptake/release of Pb2+ ions in/from SBA-15/PANI/PSS composite film was successfully achieved by modulating the redox states of the electroactive composite film, and the composite film exhibited different ion exchange behaviors at different scan rates. Based on these results, the ion exchange mechanism was proposed. Compared with the PANI/PSS composite film, the SBA-15/PANI/PSS composite film had higher adsorption capacity as well as higher selectivity toward Pb2+ ions, which should be attributed to the 3D porous morphology of the composite film with more active sites in the mesoporous SBA-15. Remarkably, the film maintained a high stability over 97% even after 500 successive cycles. It is expected that this SBA-15/PANI/PSS composite film can serve as a promising electroactive material for the effective separation of Pb2+ ions from wastewater.