A fine-grained microstructure average grain size of which is around 2 pin was developed in ZK60A magnesium alloy subjected to a FSW process. Material flow arose mainly from basal slips and was governed by simple shear deformations caused by the tool rotation. The development of the fine-grained structure was a complex process driven by severe plastic deformations, formation of deformation bands, grain splitting, twinning and dynamic and/or static recrystallizations. It appears also that the microstructural evolution depended on morphology of fine dispersoids. [doi:10.2320/matertrans.MRA2008192]
- 出版日期2009-3