About some corrosion mechanisms of AZ91D magnesium alloy

作者：Ballerini G^*; Bardi U; Bignucolo R; Ceraolo G

来源：Corrosion Science, 2005, 47(9): 2173-2184.

DOI：10.1016/j.corsci.2004.09.018

• magnesium
• weight loss
• X-ray photoelectron spectra

The present work is dedicated to a study of the corrosion resistance of AZ91D (91% Mg) alloy in wet environments. Three industrial alloys obtained by die-casting or sand casting were subjected to salt spray corrosion tests (ASTM-B117 standard) and immersion tests. Weight loss kinetic curves were measured. Surface analysis was performed by X-ray photoelectron diffraction (XPS). After corrosion the sand cast alloy presents a surface mainly enriched in hydroxides and carbonates while the die-cast alloy presents a surface enriched also in mixed Mg-Al oxides. The quantitative analysis of the rate Mg/Al shows an enrichment in aluminium for the die-cast alloys in comparison to the sand cast alloy.

• 出版日期2005-9