Development of nanostructured SUS316L-2%TiC with superior tensile properties

作者：Sakamoto T^*; Kurishita H; Matsuo S; Arakawa H; Takahashi S; Tsuchida M; Kobayashi S; Nakai K; Terasawa M; Yamasaki T; Kawai M

来源：Journal of Nuclear Materials, 2015, 466: 468-476.

DOI：10.1016/j.jnucmat.2015.08.027

• SUS316L
• TiC
• Radiation resistance
• Nanostructures
• Tensile property
• Phase transformation
• M-d point

Structural materials used in radiation environments require radiation tolerance and sufficient mechanical properties in the controlled state. In order to offer SUS316L austenitic stainless steel with the assumed requirements, nanostructured SUS316L with TiC addition of 2% (SUS316L-2TiC) that is capable of exhibiting enhanced tensile ductility and flow strength sufficient for structural applications was fabricated by advanced powder metallurgical methods. The methods include MA (Mechanical Alloying), HIP (Hot Isostatic Pressing), GSMM (Grain boundary Sliding Microstructural Modification) for ductility enhancement, cold rolling at temperatures below M-d (the temperature where the martensite phase occurs by plastic deformation) for phase transformation from austenite to martensite and heat treatment for reverse transformation from martensite to austenite. It is shown that the developed SUS316L-2TiC exhibits ultrafine grains with sizes of 90-270 nm, accompanied by TiC precipitates with 20-50 nm in grain interior and 70-110 nm at grain boundaries, yield strengths of 1850 to 900 MPa, tensile strengths of 1920 to 1100 MPa and uniform elongations of 0.6-21%, respectively, depending on the heat treatment temperature after rolling at -196 degrees C.

• 出版日期2015-11