Novel surface treatment for hydrogen storage alloy in Ni/MH battery

作者：Zhao, Xiangyu; Ma, Liqun^*; Ding, Yi; Yang, Meng; Shen, Xiaodony

来源：International Journal of Hydrogen Energy, 2009, 34(8): 3506-3510.

DOI：10.1016/j.ijhydene.2009.02.033

• Surface treatment
• Hydrogen storage
• Ni-B
• High rate dischargeability

A novel surface treatment for the MlNi(3.8)Co(0.75)Mn(0.4)Al(0.2) (La-rich mischmetal) hydrogen storage alloy has been carried out by using an aqueous solution of HF and KF with a little addition of KBH4. The results of scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) showed that rough surface was formed and Al was partly dissolved into the solution after the treatment. The result of XPS indicated the formation of Ni3B and LaF3 compounds on the alloy surface by the treatment. The probable chemical reaction mechanism for the surface treatment was introduced. The treatment resulted in significant improvements in the activation property, discharge capacity and cycle life of the alloy, especially the high rate dischargeability (HRD). The HRD of the treated alloy still remained 54.9% while that of the untreated one was only 15.1% at a discharge current density of 1200 mA/g.

• 出版日期2009-5
• 单位南京工业大学