摘要
Highly crystalline CoFe2O4 nanoparticles with different diameters ranging from 2.4 to 6.1 nm have been synthesized by forced hydrolysis in polyol. The size can be controlled through adjusting the nominal water/metal molar ratio. X-ray diffraction, transmission electron microscopy, x-ray absorption spectroscopy and Fe-57 Mossbauer spectrometry were employed to investigate the structure and the microstructure of the particles produced. Magnetic measurements performed on these particles show that they are superparamagnetic with a size-dependent blocking temperature. At 5 K, high saturation magnetization (similar to 85 emu g(-1)) approaching that of the bulk was found for the larger particles, whereas a very large coercivity (14.5 kOe) is observed for the 3.5 nm sized particles.
- 出版日期2011-12-21