Antisolvent crystallization and solid-state polymerization of bisphenol-A polycarbonate

作者：Chang, Xuesong; Ding, Tongmei; Tian, Hengshui^*; Wang, Tiantian

来源：Journal of Applied Polymer Science, 2016, 133(27): 43636.

DOI：10.1002/app.43636

• crystallization
• polycarbonates
• polycondensation

Bisphenol-A polycarbonate (BAPC) was synthesized by solid-state polymerization (SSP) using a semicrystalline prepolymer crystallized by antisolvent method. The antisolvent crystallization was investigated as a function of antisolvent types using X-ray diffraction (XRD), different scanning calorimetry (DSC), and scanning electron microscopes (SEM). The results showed antisolvent types had a significant effect on the crystallization of BAPC. Prepolymer induced by acetone as an antisolvent gained a higher crystallinity of 37.0%, more uniform particle size, and mature crystal structure compared with the samples crystallized by methanol and ethanol. Then crystallization of BAPC by acetone was carried out at crystallization temperature in the range of 40-80 degrees C for 1-5 h. A high crystallinity of 42.0% was acquired with the crystallization conducted at 70 degrees C for 2 h. Prepolymer with appropriate crystallinity of 37.8% resulted in high-molecular-weight polymer of 57,411 via SSP due to the effect of crystallinity and plasticization of residual solvent.

• 出版日期2016-7-15
• 单位华东理工大学