Ni-P amorphous phases obtained by Nd-YAG pulsed laser alloying of deposited Ni-P coating with aluminum

作者：Yang Y; Hu JD; Wang HY; Liu SY; Li Y; Guo ZX^*

来源：Materials Letters, 2006, 60(9-10): 1128-1130.

DOI：10.1016/j.matlet.2005.10.087

• coating
• TEM
• amorphous

Ni-P electroless deposited coating with crystalline morphology was prepared on aluminum substrate. A Nd-YAG pulsed laser was used to alloy the materials at the condition of power density 5.36 x 10(9) W/m(2) and scanning speed 3.0 mm/s. In the laser alloyed layer, Ni-P amorphous phases were found by means of TEM. Electron diffraction patterns and X-ray diffraction results showed that these Ni-P amorphous phases were decomposed as Ni and Ni3P equilibrium phases when tempered at temperature over 300 degrees C.