A CeFeOx catalyst for catalytic oxidation of NO to NO2

作者：Wang Wenhuan; Li Wei; Guo Ruitang^*; Chen Qilin; Wang Qingshan; Pan Weiguo^*; Hu Guoxin

来源：Journal of Rare Earths, 2016, 34(9): 876-881.

DOI：10.1016/S1002-0721(16)60109-6

• NO
• catalytic oxidation
• CeFeOx catalyst
• characterization
• rare earths

Catalytic oxidation of NO into NO2 is a promising method for NOx emission control. The aim of this study was to develop an economic and environmental-friendly catalyst for NO catalytic oxidation. Herein a CeFeOx complex oxide catalyst for catalytic oxidation of NO was prepared by coprecipitation method. After that the catalytic performance of this catalyst was measured on a fixed-bed reactor. It was found that the intrinsic activity of CeFeOx was higher than that of CeOx and FeOx. The characterization techniques of Brumauer-Emmett-Teller (BET), X-ray diffraction (XRD), temperature programmed reduction with H-2 (H-2-TPR), temperature programmed desorption with NO+O-2 (NO+O-2-TPD) and X-ray photoelectron spectroscopy (XPS) were performed to investigate the surface area, crystal structure, redox property and NOx adsorption behavior of the catalyst samples. From the characterization results, it was concluded that the low crystallinity of CeFeOx promoted the dispersion of active species, as a result, enhancing the redox ability and NO adsorption capacity of CeFeOx catalyst, which is favorable to NO catalytic oxidation. Furthermore, the presence of much chemisorbed oxygen on CeFeOx catalyst also made a great contribution to its good catalytic performance.

• 出版日期2016-9
• 单位上海电力大学; 上海交通大学