A novel flower-like nickel borate of Ni3B2O6 nanostructure was prepared through a hydrothermal treatment and sequential thermal decomposition of precursor without employing any template or surfactant. All the samples were characterized by XRD, IR, XPS, TG-DTA, nitrogen adsorption, SEM and TEM. The flower-like Ni3B2O6 nanostructure was self-assembled by nanosheets with the thickness of about 40 nm. The electrochemical properties in lithium-ion battery of flower-like Ni3B2O6 nanostructure were studied by the cyclic voltammetry, galvanostatic cycling test, and electrochemical impedance spectroscopy, which showed it had a high initial discharge capacity and a good reversibility.
- 出版日期2014-11
- 单位陕西师范大学