HMPT-BOF-RH-CSP process for SPHE substrate of cold rolled deep drawing steel

作者：Wu Guang-liang^*; Meng Zheng-bing; Zhou Chao-yang; Liu Xin-bin; Huang Tao

来源：Journal of Central South University, 2013, 20(4): 871-876.

DOI：10.1007/s11771-013-1560-5

• hot metal pretreatment
• basic oxygen furnace
• compact strip production
• deep drawing
• hardening exponent
• plastic strain ratio

Based on hot metal pretreatment (HMPT)-basic oxygen furnace (BOF)-Rheinstahl Heraeus (RH)-compact strip production (CSP) process, parameters controlling on cold rolling deep drawing substrate SPHE were investigated during smelting and rolling process by composition design and technology control. The influence of parameters on chemical compositions, mechanical properties and microstructure was revealed by scanning electron microscope (SEM). The results show that, 1) main chemical components in SPHE are w(C)<= 40x10 (6), w(Si)<= 0.01%, w(S)<= 0.009%, w(N)<= 20x10 (6), w(O)<= 25x10 (6); 2) main mechanical properties of the SPHE are sigma(s)=274 MPa, sigma(b)=334 MPa, A=48.9%; 3) main performances of deep drawing quality (DDQ) grade steel produced by SPHE are as follows, transversely sigma(s)=167 MPa, sigma(b)=298 MPa, n=0.219, r=2.46; vertically sigma(s)=166 MPa, sigma(b)=298 MPa, n=0.226, r=2.39; in 45 degrees direction sigma(s)=171 MPa,sigma(b)=308 MPa, n=0.214, r=2.26; 4) microstructure of DDQ is ferrite, average grain size is Grade 7.5, and inclusion size is 3-10 mu m.

• 出版日期2013-4
• 单位中南大学