Microwave surface resistance of YBCO superconducting thin films under high DC magnetic field

作者：Honma T; Sato S; Sato K; Watanabe M; Saito A; Koike K; Kato H; Ohshima S^*

来源：Physica C-Superconductivity and Its Applications, 2013, 484: 46-48.

DOI：10.1016/j.physc.2012.03.035

• Surface resistance
• High dc magnetic field
• YBa2Cu2Oy
• Thin film

We investigated the dc magnetic field and temperature dependences of the microwave surface resistance (R-s) of YBa2Cu3Oy (YBCO) superconducting thin films with various thicknesses. We used YBCO thin films with 300, 500, and 700 nm deposited on a MgO (100) substrate by the thermal co-evaporation method. The R-s was measured using the dielectric resonator method at 21.8 GHz, and a high dc magnetic field of up to 12 T was applied parallel to the c-axis of the YBCO thin films during R-s measurements. The R-s value of YBCO thin films increased when dc magnetic field was applied. These relationships could be explained by using the two-fluid model for high frequency and low magnetic field limits. We defined the viscous drag coefficient eta under the low magnetic limit and the high magnetic field limit as the eta(low) (B, T, d) and eta(high) (B, T, d), respectively. The eta(low) values were approximately two orders of magnitude greater than eta(high) values. Also, all eta(low) and eta(high) value decreased or saturated as the temperature and film thickness increased. These results show that eta under the low and high magnetic field limit depended on the temperature and film thickness.

• 出版日期2013-1