Dependence of the MgO sputtering power on the characteristics of MgZnO thin films grown by radio-frequency magnetron sputtering

作者：Moon Jin Young; Lee Ho Seong^*; Kim Young Yi; Cho Hyung Koun; Kim Hong Seung

来源：Thin Solid Films, 2009, 518(4): 1230-1233.

DOI：10.1016/j.tsf.2009.06.058

• MgZnO
• Co-sputtering
• MgO interfacial layer
• TEM

The dependence of the MgO sputtering power on the structural and optical properties of epitaxially grown MgZnO thin films on GaN/sapphire substrates by radio-frequency magnetron sputtering was investigated. The photoluminescence investigation showed blue shift of 170 meV in MgZnO film grown at the MgO power of 300 W, compared with the ZnO films grown at the MgO power of 0 W, which was attributed to the enhancement of the Mg incorporation at higher power. In addition, increase in Mg mole fraction with increase in sputtering power of MgO was observed from the PL results, and a maximum of 6.6 at.% Mg was obtained at the MgO power of 300 W. The high-resolution X-ray diffraction and transmission electron microscopy (TEM) investigations revealed that the threading dislocation density in the MgZnO thin films increased with increase in sputtering power. Furthermore, microstructural analysis performed by TEM revealed formation of a thin cubic-like phase in the interface between GaN template and MgZnO thin film, together with increased thickness of the interfacial layer with sputtering power.

• 出版日期2009-12-15