Material development for grade X80 heavy-wall hot induction bends

作者：Wang, Xu; Xiao, Fu-ren; Fu, Yan-hong; Chen, Xiao-wei; Liao, Bo^*

来源：Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 2011, 530: 539-547.

DOI：10.1016/j.msea.2011.10.017

• Pipeline steel
• Hot induction bend
• Heat treatment
• Microstructure
• Mechanical property

A new steel for grade X80 heavy wall thickness hot induction bends was designed based on the chemical compositions of commercial X80 steels in this work. Then, its continuous cooling transformation (CCT) diagram was determined with Gleeble-3500 thermo-mechanical simulator. Furthermore, the effects of heat treatment technology on its microstructure and mechanical property were investigated, and the technology parameters of the heat treatment were optimized. The results show that the acicular ferrite and/or bainite transformations are promoted, the polygonal ferrite and pearlite transformation are restrained, because proper amount of alloying elements were added into the new steel. Therefore, the strength of this new steel is improved markedly, even if the cooling rate is lower, which ensure the higher strength distribution along cross section of the heavy wall thickness. It is significant for the manufacture of grade X80 heavy wall thickness hot induction bends in the second West-to-East gas transportation pipeline project of China.

• 出版日期2011-12-15
• 单位燕山大学