(100) Three-Axis-Oriented BaTiO3, (Ba0.7Sr0.3)TiO3 Thin Film Prepared by Chemical Solution Deposition Method

作者：Hosokura Tadasu^*; Kageyama Keisuke; Takagi Hiroshi; Sakabe Yukio

来源：International Journal of Applied Ceramic Technology, 2012, 9(1): 74-82.

DOI：10.1111/j.1744-7402.2011.02668.x

Epitaxially grown (100) three-axis-oriented (Ba0.7Sr0.3)TiO3 thin film on (100) platinum (Pt) coated (100) magnesium oxide (MgO) substrate and (100) three-axis-oriented BaTiO3 thin film with BaZrO3 buffer layer were prepared on an MgO(100) substrate using the chemical solution deposition method. The growth of the film was found to depend on the annealing condition. Transmission electron microscope revealed cube-on-cube epitaxial growth. The thin films exhibited a (100) three-axis-orientation that followed the (100) orientation of the MgO substrate and the (100) orientation of the Pt or BaZrO3 bottom layer, as observed from an X-ray pole figure measurement and the selected area electron diffraction patterns.

• 出版日期2012-2