Anomalous optical and magnetic behavior of multi-phase Mn doped Zn2SiO4 nanowires: a new class of dilute magnetic semiconductors

作者：Hafeez Muhammad; Ali Awais; Manzoor Sadia; Bhatti Arshad S^*

来源：Nanoscale, 2014, 6(24): 14845-14855.

DOI：10.1039/c4nr03501a

We present the synthesis of Mn doped Zn2SiO4 dense nanowire bundles using the VLS mode of growth with unusual optical and magnetic properties. The synthesized Zn2SiO4 nanowires were identified with two phases, alpha-Zn2SiO4 as the major phase and beta-Zn2SiO4 as the minor phase. XPS studies confirmed that Zn2SiO4 nanowires were Zn rich and Mn doped. Temperature dependent photoluminescence (PL) measurements showed three distinct emission bands: green, yellow and red due to Mn doping in the alpha-phase, beta-phase and the substitution of Si with Mn in the alpha-phase, respectively. The PL analysis showed that these emission bands followed anomalous Berthelot-type behavior. The carrier escape energies were 70 +/- 3 meV, 49 +/- 2 meV and 65 +/- 4 meV for the 530, 570 and 660 nm bands, respectively, while the radiation rates (E-r =) were 1.0 +/- 0.4 meV, 3.10 +/- 1.10 meV and 1.4 +/- 0.4 meV corresponding to the three respective bands. Mn doping of Zn2SiO4 nanowires induced ferromagnetism, which was observed above room temperature, with a Curie temperature well above 380 K. The observation of magnetic behavior in this class of semiconductors has potential applications in high temperature spintronics and magneto-optical devices.

• 出版日期2014