Atomistic simulation study of brittle failure in nanocrystalline graphene under uniaxial tension

作者：Cao Ajing^*; Qu Jianmin

来源：Applied Physics Letters, 2013, 102(7): 071902.

DOI：10.1063/1.4793088

We show that, using molecular dynamic simulations, nanocrystalline (NC) graphene fails by brittle fracture along grain boundaries under uniaxial tension at room temperature. Initiated from either a grain-boundary triple junction or an array of vacancies on a preferential grain boundary, fracture occurs by unzipping atomic bonds along a preferential grain boundary. In sharp contrast to NC metals, no mobile dislocations are generated throughout the entire loading process, and the deformation remains fully elastic (albeit nonlinear) until the breaking of the first atomic bond due to high local stress near the initiation defect sites. Breaking of the first atomic bond triggers a cascade of bond breaking events along a preferential grain boundary that leads to the final brittle fracture failure. For the NC graphene monolayer sheet with an average grain size of similar to 25nm considered here, the predicted uniaxial tensile strength is 96.2+/-4.2GPa, which is one of the highest among all polycrystalline materials.

• 出版日期2013-2-18
• 单位西北大学