Phosphorous acid route synthesis of iron tavorite phases, LiFePO4(OH)(x)F1-x [0 %26lt;= x %26lt;= 1] and comparative study of their electrochemical activities

作者：Asl Hooman Yaghoobnejad; Choudhury Amitava^*

来源：RSC Advances, 2014, 4(71): 37691-37700.

DOI：10.1039/c4ra05391e

New synthesis routes were employed for the synthesis of three derivatives of iron hydroxo-, fluoro-, and mixed hydroxo-fluoro phosphates LiFePO4(OH)(x)F1-x where 0 %26lt;= x %26lt;= 1 with the tavorite structure type, and their detail electrochemical activities have been presented. The hydrothermal synthesis of the pure hydroxo-derivative, LiFePO4OH, using phosphorous acid as a source of phosphate yielded good quality crystals from which the crystal structure was solved for the first time using SC-XRD (single crystal X-ray diffraction). The fluoro derivative, LiFePO4F, was prepared as a very fine powder at low temperature in a solvent-less flux-based method employing phosphorous acid and mixed alkali metal nitrates. A mixed anionic hydroxo-fluoro iron tavorite phase, LiFePO4(OH)(0.32)F-0.68, was also synthesized by a hydrothermal route. The electrochemical performance of the three phases was studied with galvanostatic charge-discharge tests, cyclic voltammetry, and electrochemical impedance spectroscopy (EIS). All three phases showed facile Li-insertion through the reduction of Fe3+ to Fe2+ at an average voltage in the range of 2.4-2.75 V, through the variation of the anion from pure OH to pure F. An increase of 0.35 V was observed as a result of F substitution in the OH position. Also, good cyclability and capacity retention were observed for all three phases and a reversible capacity of more than 90% was achieved for LiFePO4F. The results of EIS indicated that lithium ion mobility is highest in the mixed anion.

• 出版日期2014