摘要
Alumina (Al2O3) decorated anatase TiO2 nanotubes with ordered mesoporous pore walls (Al2O3/meso-TiO2 nanotubes) are successfully synthesized through vacuum pressure induction technology, and then combined with the thermal decomposition of a mesoporous TiO2 sol precursor, inside the cylindrical nanochannels of an anodic aluminium oxide (AAO) template. The decorated Al2O3 was formed by in situ deposition via direct reaction of the strong acid sol precursor and the nanochannel wall of the AAO template. The resultant Al2O3/meso-TiO2 nanotubes are characterized in detail by transmission electron microscopy, scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, Raman spectroscopy, and N-2 adsorption-desorption. The experimental results reveal that the Al2O3/meso-TiO2 nanotubes have a tubular structure with an average diameter of similar to 200 nm and highly ordered mesopores in the tubular walls. The Al2O3 is distributed evenly on the anatase TiO2 nanotubes. Moreover, the Al2O3/meso-TiO2 nanotubes possess a large specific surface area (136 m(2) g(-1)) and narrow mesopore size distribution (similar to 10 nm). By using NOx as a probe molecule, the Al2O3/meso-TiO2 nanotube films exhibit better sensing performance than that of mesoporous TiO2 nanotubes, in terms of their high sensitivity, fast response-recovery time, and good stability in air at room temperature. The outstanding performance in the gas sensing ability of Al2O3/meso-TiO2 nanotubes is a result of their one-dimensional tubular and mesoporous nanostructures, advantageous for the adsorption and diffusion of NOx gas. In addition, the sensing response is greatly improved by virtue of the decorated Al2O3 on the surfaces of the TiO2 nanotubes, which acts as an energy barrier to suppress charge recombination. The structural properties of the Al2O3/meso-TiO2 nanotubes makes them a viable novel gas sensor material at room temperature.