A spectroscopic and microstructural study of oxide coatings produced on a Ti-6Al-4V alloy by plasma electrolytic oxidation

作者：Hussein R O; Nie X; Northwood D O^*

来源：Materials Chemistry and Physics, 2012, 134(1): 484-492.

DOI：10.1016/j.matchemphys.2012.03.020

• Ti-6Al-4V alloy
• Plasma electrolytic oxidation (PEO)
• Ceramic coatings
• Corrosion

In this study, we have used PEO (plasma electrolytic oxidation) for the production of oxide coatings on a Ti-6Al-4V alloy at two different current modes, namely pulsed unipolar and bipolar. Optical emission spectroscopy (OES) in the visible and near UV band (280-800 nm) was used to characterize the PEO plasma. The emission spectra were recorded and the plasma temperature profile versus processing time was constructed using a line intensity ratios method. The aim of this work was to study the effect of the process parameters, including current mode and pulse duration time, on the plasma characteristics, surface morphology and microstructure and corrosion resistance of oxides grown on Ti-6Al-4V by PEO process. Scanning electron microscopy (SEM) with energy dispersive X-ray analysis (EDS) and X-ray diffraction (XRD) were used to study the coating microstructure, morphology and phase composition. The corrosion resistance of the coated and uncoated samples was examined by potentiodynamic polarization in a 3.5% NaCl solution. It was found that the plasma temperature profiles are significantly influenced by changing the current mode from unipolar to bipolar. The strongest discharges that are initiated at the interface between the substrate and the coating can be reduced or eliminated by using a bipolar current mode. This produces a thinner, denser and more corrosion-resistant coating.

• 出版日期2012-5-15