Duplex surface treatment of AISI 1045 steel via plasma nitriding of chromized layer

作者：Hakami F; Sohi M Heydarzadeh^*; Ghani J Rasizadeh

来源：Thin Solid Films, 2011, 519(20): 6792-6796.

DOI：10.1016/j.tsf.2011.04.054

• Duplex treatment
• Chromizing
• Plasma nitriding
• Chromium nitride
• Steel

In this work AISI 1045 steel were duplex treated via plasma nitriding of chromized layer. Samples were pack chromized by using a powder mixture consisting of ferrochromium, ammonium chloride and alumina at 1273 K for 5 h. The samples were then plasma-nitrided for 5 h at 803 K and 823 K. in a gas mixture of 75%N(2)+25%H(2). The treated specimens were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) analysis and Vickers micro-hardness test. The thickness of chromized layer before nitriding was about 8 pm and it was increased after plasma nitriding. According to XRD analysis, the chromized layer was composed of chromium and iron carbides. Plasma nitriding of chromized layer resulted in the formation of chromium and iron nitrides and carbides. The hardness of the duplex layers was significantly higher than the hardness of the base material or chromized layer. The main cause of the large improvement in surface hardness was due to the formation of Cr(x)N and Fe(x)N phases in the duplex treated layers. Increasing of nitriding temperature from 803 to 823 K enhanced the formation of CrN in the duplex treated layer and increased the thickness of the nitrided layer.

• 出版日期2011-8-1