Composition and size dependence of magnetic properties of FePt/Fe exchange-spring films

作者：Song, Yu; Zhang, Zhe; Duan, Nian; Wang, Jiawei; Chen, Yuang; Tong, Bei; Yang, Xiaofei; Zhang, Yue^*

来源：Journal of Magnetism and Magnetic Materials, 2014, 371: 100-105.

DOI：10.1016/j.jmmm.2014.07.029

• Magnetic properties
• FePt/Fe
• Exchange-spring
• Micromagnetic simulation

The composition and size dependence of the magnetic properties of FePt/Fe exchange-spring bilayer films was studied using micromagnetic simulation. Based on the simulated hysteresis loops for composite layers with an identical thickness of 20 am and different composition ratios, it can be observed that when the thickness ratio of Fe is 10%, an exchange-spring effect with a negative nucleation field appears; the switching field is greatly reduced compared to the rigid magnetic FePt, and the squareness ratio reaches its maximum value. When the thickness ratio of Fe is 25% and more, the nucleation fields become positive; meanwhile, the coercivity is smaller than the switching field, and the squareness ratio decreases because of the increase in the thickness of the Fe film. In addition, at a Fixed thickness ratio and total volume, the switching field of the FePt/Fe bilayer films is further reduced, accompanied by a decrease in the squareness ratio due to an increase in the thickness of the Fe layer.

• 出版日期2014-12
• 单位华中科技大学