Development and characterization of lithium-releasing silicate bioactive glasses and their scaffolds for bone repair

作者：Miguez Pacheco V; Buettner T; Macon A L B; Jones J R; Fey T; de Ligny D; Greil P; Chevalier J; Malchere A; Boccaccini A R^*

来源：Journal of Non-Crystalline Solids, 2016, 432: 65-72.

DOI：10.1016/j.jnoncrysol.2015.03.027

Incorporation of therapeutic ions into the structure of bioactive glasses for direct stimulation of cells is a very attractive approach for tissue engineering strategies. Lithium has recently been identified as a biologically active ion which can stimulate osteoblast cell activity. In this study, lithium-containing bioactive glasses (Li-BGs) where Li2O substitutes Na2O in different amounts (2.5, 5 and 10 wt.% Li2O) in 45S5 bioactive glass (BC) were produced and made into 3D scaffolds by the foam replica method. The structural changes that occur after heat treatment, the effect of lithium-content on the bioactivity of the glasses and their lithium ion release profiles were investigated. The results show that the novel Li-BC formulations exhibit the formation of an apatite-like layer on their surface after immersion in SBF for 1 day thus confirming their high surface reactivity, similar to undoped 45S5 BC. XRD results showed that the Li-doped BGs crystallize mainly to combeite (Na2Ca2Si3O9) and silicorhenanite (SiO4(PO4)(2)Ca-5) but also Li6P6O18 and Li3PO4 phases were detected. In terms of lithium ion release, the formulations at 2.5 wt.% and 5 wt.% Li2O content were the only ones to be within the therapeutic range (<83 ppm).

• 出版日期2016-1-15