Aqueous-solution-processable metal oxides for high-performance organic and perovskite solar cells

作者：Lou, Yan-Hui; Wang, Zhao-Kui^*

来源：Nanoscale, 2017, 9(36): 13506-13514.

DOI：10.1039/c7nr04692h

• POLYMER PHOTOVOLTAIC CELLS
• HOLE INTERFACIAL LAYER
• VANADIUM-OXIDE
• HALIDE PEROVSKITES
• LOW-TEMPERATURE
• SMALL-MOLECULE
• BUFFER LAYER
• EFFICIENCY
• CRYSTALLIZATION
• LIGHT

Poly(3,4-ethylene dioxythiophene): poly(4-styrenesulfonate) (PEDOT:PSS) is a widely utilized hole-transporting material (HTM) in planar photovoltaic devices, such as organic solar cells (OSCs) and perovskite solar cells (PSCs). However, the hygroscopic nature of PEDOT: PSS aqueous dispersions may restrict their future application. Therefore, it is necessary to develop other effective and stable HTMs to achieve high-performance photovoltaic devices. Herein, we demonstrate a facile route to deposit solution-processed MoO3, GeO2, V2O5 and CrO3 thin films as hole-transporting layers by directly dissolving their commercial powders in deionized water. Among these, the solution-processed V2O5 (sV(2)O(5)) film exhibited the highest work function of 5.2 eV, and the best hydrophobicity, with a contact angle of 77.2 degrees. The sV(2)O(5)-based OSCs and PSCs presented power conversion efficiencies (PCEs) of 8.36% and 14.13%, respectively. Notably, the PEDOT: PSS V2O5 composite HTM based device obtained a maximum PCE of 18.03% with a V-oc exceeding 1.0 V. These aqueous-solution-processed HTMs have potential applications in green and low-cost photovoltaic devices by virtue of their simple and ecofriendly preparations.

• 出版日期2017-9-28
• 单位苏州大学