Superior high-temperature oxidation resistance of magnetron sputtered Hf-B-Si-C-N film

作者：Zeman P^*; Zuzjakova S; Mares P; Cerstvy R; Zhang M; Jiang J; Meletis E I; Vlcek J

来源：Ceramics International, 2016, 42(4): 4853-4859.

DOI：10.1016/j.ceramint.2015.11.171

• Hf-B-Si-C-N
• High-temperature material
• Superior oxidation resistance
• Nanocomposite oxide layer
• Protective coating

A hard and optically transparent amorphous Hf7B23Si17C4N45 film with a contamination level less than 4 at%, prepared by reactive pulsed de magnetron sputtering, was subjected to systematic investigation of high-temperature oxidation behavior in air up to 1700 degrees C. We focus on thermogravimetric analysis of the film in air and on the evolution of the film structure, microstructure and elemental composition with an annealing temperature ranging from 1100 degrees C to 1700 degrees C. The film exhibits a superior oxidation resistance up to 1600 degrees C due to a formation of a nanocomposite protective oxide layer on the surface above 1000 degrees C. The layer consists of monoclinic and tetragonal (or orthorhombic) HfO2 nanocrystallites surrounded by a SiO2-based amorphous matrix, most probably containing boron. The HfO2 nanocrystallites exhibit a gradient in size with a dense population of small (a couple of nm) crystallites next to the interface and larger but dispersed crystallites close to the surface.

• 出版日期2016-3