Monitoring F, F+ and F-2(2+) related intense defect emissions from nanocrystalline MgO

作者：Choudhury Biswajit^*; Basyach Priyanka; Choudhury Amarjyoti

来源：Journal of Luminescence, 2014, 149: 280-286.

DOI：10.1016/j.jlumin.2014.01.041

• Oxygen defects
• F-centers
• Absorption
• Luminescence

MgO contains several oxygen defect related absorption peaks in the UV as well as in the visible region. The emission spectra are obtained at three different excitations, 6.02 eV (206 nm), 4.59 eV (270 nm) and 3.75 eV (330 nm) respectively. Each excitation results in an intense emission associated with F+, F-2(2+) and F-type oxygen defect centers. These intense defect emissions mostly appear in the UV and visible region of the energy spectrum. Since the emission peaks are associated with oxygen vacancies, annealing at 800 degrees C reduces the intensity of these peaks. The ratio of the emission intensity of F+/F and F+/F-2(2+) decreases at 800 degrees C, whereas F/F-2(2+) intensity ratio increases at 800 degrees C. It is anticipated that thermal conversion of F+ and F-2(2+) to F centers at 800 degrees C results in the enhancement of F/F-2(2+) emission intensity ratio at high temperature.

• 出版日期2014-5