Preparation and characterization of indium tin oxide films formed by oxygen ion beam assisted deposition

作者：Liu C^*; Mihara T; Matsutani T; Asanuma T; Kiuchi M

来源：Solid State Communications, 2003, 126(9): 509-513.

DOI：10.1016/S0038-1098(03)00237-0

• indium tin oxide
• ion beam assisted deposition

Indium tin oxide (ITO) films were produced by low-energy oxygen ion beam assisted electron-beam evaporation. The dependence of surface morphology, electrical and optical properties on evaporation rate, oxygen ion beam energy and density, as well as substrate temperatures was characterized by atomic force microscopy, X-ray photoelectron spectroscopy, Hall-effect and optical transmittance measurements. The results show that high-quality ITO films (resistivity of 7.0 X 10(-4) Omega cm, optical transmittance above 85% at wavelength 550 nm, surface roughness of 0.6 nm in root mean square) can be obtained at room temperature.

• 出版日期2003-5
• 单位武汉大学