Ductile PLA nanocomposites with improved thermal stability

作者：Chen Bor Kuan^*; Shih Chien Chang; Chen Antonia F

来源：Composites Part A: Applied Science and Manufacturing , 2012, 43(12): 2289-2295.

DOI：10.1016/j.compositesa.2012.08.007

• Polymer-matrix composites
• Mechanical properties
• Thermal properties
• Polylactide

Polylactide (PLA) is used as a biomedical material because it is biodegradable, but the vast majority of biodegradable polymers in clinical use are composed of rather stiff materials that are unsuitable for use in numerous applications because they exhibit limited extendibility, weak mechanical strength, and poor thermal stability. We modified PLA with 2-methacryloyloxyethyl isocyanate (MOI) to prepare ductile PLA materials. By utilizing a novel sol-gel process, PLA nanocomposites were further prepared with improved mechanical properties and thermal stability. The 10% thermal decomposition temperature for PLA modified with 5% MOI and 5-10% silica was 21-32 degrees C higher than that of original pristine PLA. Elongation at break increased by 4-13 times when compared to neat PLA while the tensile strength was maintained at 30-40 MPa. These synthesized PLA nanocomposites can be applied as biomaterials with improved mechanical and thermal properties.

• 出版日期2012-12