The impact of Si/Al ratio on properties of aluminosilicate aerogels

作者：Shalygin Anton S^*; Kozhevnikov Ivan V; Gerasirnov Evgeny Yu; Andreev Andrey S; Lapina Olga B; Martyanov Oleg N

来源：Microporous and Mesoporous Materials, 2017, 251: 105-113.

DOI：10.1016/j.micromeso.2017.05.053

• Aluminosilicate
• Aerogels
• Si/Al ratio
• Sol-gel method
• Supercritical drying

The Si/Al ratio is a key parameter of acid-base, structural, textural and, consequently, catalytic properties of amorphous crystalline (micro- and mesoporous) aluminosilicates. The changes of structural and textural characteristics of Al-Si aerogels with gradual increase of aluminum content are investigated. Aerogels were prepared via sol-gel method using prehydrolysed tetraethoxysilane and aluminium isopropoxide stabilized by acetylacetone. The gelation of the obtained sols took place in the presence of ammonia with the following drying in supercritical isopropanol. It was shown all aluminum reacts with prehydrolyzed tetraethoxysilane forming spherical particles in case the content of Al in the samples is less than 20 mol %. Aluminum drives the increase of interparticle coupling leading to the particle agglomeration, which is associated with the increase of the particle size and decrease of specific surface area and pore volume. For the samples with the aluminum content of >50 mol % the formation of pseudoboehmite plate-like particles is observed. The pseudoboehmite particles prevent the sintering of SiO2 particles that leads to the increase of the aerogel specific surface area and pore volume. In case the high aluminum content (>80 mol %) the silica particles serve as a connector between boehmite plates. The ratio between Bronsted and Lewis acid sites decreases gradually with the increase of aluminum content of the aluminosilicate aerogels.

• 出版日期2017-10