Asymmetric quantum-well structures for AlGaN/GaN/AlGaN resonant tunneling diodes

作者：Yang, Lin'an^*; Li, Yue; Wang, Ying; Xu, Shengrui; Hao, Yue

来源：Journal of Applied Physics, 2016, 119(16): 164501.

DOI：10.1063/1.4948331

• TRAPS

Asymmetric quantum-well (QW) structures including the asymmetric potential-barrier and the asymmetric potential-well are proposed for AlGaN/GaN/AlGaN resonant tunneling diodes (RTDs). Theoretical investigation gives that an appropriate decrease in Al composition and thickness for emitter barrier as well as an appropriate increase of both for collector barrier can evidently improve the negative-differential-resistance characteristic of RTD. Numerical simulation shows that RTD with a 1.5-nm-thick GaN well sandwiched by a 1.3-nm-thick Al0.15Ga0.85N emitter barrier and a 1.7-nm-thick Al0.25Ga0.75N collector barrier can yield the I-V characteristic having the peak current (Ip) and the peak-to-valley current ratio (PVCR) of 0.39A and 3.6, respectively, about double that of RTD with a 1.5-nm-thick Al0.2Ga0.8N for both barriers. It is also found that an introduction of InGaN sub-QW into the diode can change the tunneling mode and achieve higher transmission coefficient of electron. The simulation demonstrates that RTD with a 2.8-nm-thick In0.03Ga0.97N sub-well in front of a 2.0-nm-thick GaN main-well can exhibit the I-V characteristic having Ip and PVCR of 0.07A and 11.6, about 7 times and double the value of RTD without sub-QW, respectively. The purpose of improving the structure of GaN-based QW is to solve apparent contradiction between the device structure and the device manufacturability of new generation RTDs for sub-millimeter and terahertz applications. Published by AIP Publishing.

• 出版日期2016-4-28
• 单位西安电子科技大学