Mild aqueous synthesis of octahedral Mn3O4 nanocrystals with varied oxidation states

作者：Hao, Xinli; Zhao, Jingzhe^*; Li, Yunling; Zhao, Yan; Ma, Dechong; Li, Linzhi

来源：Colloids and Surfaces A: Physicochemical and Engineering Aspects , 2011, 374(1-3): 42-47.

DOI：10.1016/j.colsurfa.2010.10.048

• Mn3O4 nanocrystal
• Aqueous synthesis
• Optical properties
• HCl sensitive

Mn3O4 nanocrystals were prepared by a simple aqueous precipitation method using Mn(CH3COO)(2)center dot 4H(2)O and NaOH as precursors at low temperature of 30 degrees C. The as-prepared Mn3O4 nanocrystals were characterized by means of XRD, SEM, UV-vis and FT-IR analyses. Mn3O4 nanoparticles prepared at 30 degrees C extended octahedral, spherical and rod-like structures with the sizes in the range of 60-100 nm. The size and shape could be manipulated by reaction time. The as-prepared Mn3O4 was so sensitive to hydrochloric acid (HCl) that the sample color changed obviously from brown to black. Analyses on the HCl treated and untreated samples gave results that varied ratio of Mn2+. Mn3+ and Mn4+ in Mn3O4 crystals led to color changes of the samples. Optical properties of the samples were discussed via the UV-vis and FT-IR results.

• 出版日期2011-1-20
• 单位吉林大学; 湖南大学