Utilization of precipitated CaCO3 from carbon sequestration of industrially emitted CO2 in cementless CaO-activated blast-furnace slag binder system

作者：Jeong Yeonung; Yum Woo Sung; Moon Juhyuk; Oh Jae Eun^*

来源：Journal of Cleaner Production, 2017, 166: 649-659.

DOI：10.1016/j.jclepro.2017.08.097

• Precipitated calcium carbonate
• CaO-Activation
• GGBFS
• CO2 storage
• Cementless binder

This study explores the use of precipitated calcium carbonate (PCC), an industrial by-product from the carbon sequestration process for emitted CO2 from factories, in the cementless CaO-activated ground granulated blast-furnace slag (GGBFS) system in an aim not only to improve the strength but also to develop more sustainable structural binder for concrete. The 28-day strength improved with increasing PCC content up to 20 wt%, and its highest strength showed an similar to 23% increase from the original strength of the sample without PCC. The analysis revealed that the PCC was not a simple inert filler, but it might promote more dissolution of GGBFS, resulting in a higher strength from additional formation of reaction products. In particular, even the sample with 50 wt% PCC yielded a very similar strength compared to the sample without PCC at 28 days. Thus, this binder system could be a decent solution that can store a large amount of PCC without a significant strength reduction.

• 出版日期2017-11-10