Adsorption of Rhodamine 6G on SiO2 and Ag@SiO2 Porous Solids: Coupling Thermodynamics and Raman Spectroscopy

作者：Fernand Deborah; Pardanaud Cedric; Berge Lefranc David; Gallice Philippe; Hornebecq Virginie^*

来源：Journal of Physical Chemistry C, 2014, 118(28): 15308-15314.

DOI：10.1021/jp503776y

The sensitive detection of small molecules analytes at very low concentrations is of great interest, notably in the medical and environmental fields. In 2000 this study, two porous solids, namely SiO2 (d(pore) approximate to 5 nm) and Ag@SiO2, were prepared. In the latter, the incorporation of Ag nanopartides in the porous matrix was highlighted using different techniques. Around 0.25 wt % of nanoparticles were inserted with a mean woo diameter close to 3 tun. Then, the adsorption of rhodamine 6G (R6G) on these two materials was studied coupling thermodynamics and Raman spectroscopy. From a thermodynamic point of view, it was shown that whereas the adsorbed amounts of R6G (N-ads) were not affected by the presence of Ag nanopartides, the adsorption enthalpies in the case of Ag@SiO2 are doubled compared to those of SiO2, highlighting the strong interaction of R6G with the Ag nanoparticle surface. Furthermore, for N-ads > 1 mu mol g(-1), it was evidenced that the Raman response of R6G, in terms of band positions and intensities, is directly related to the amounts of R6G adsorbed on the solid surface and not to the presence of Ag. This result highlights the preconcentration properties of porous solids. For N-ads = 0.05 mu mol g(-1), the intensities of Raman bands that are detected, corresponding to bending modes of ethylamine groups, are enhanced in the case of Ag@SiO2 by a factor of roughly 10. This value corresponds to the order of magnitude generally assumed for the chemical enhancement mechanism of surface enhanced Raman spectroscopy effect. This result and the high values of integral enthalpies of adsorption determined for Ag@SiO2 highlight strong interactions between amine groups and the Ag surface.

• 出版日期2014-7-17