Modification of Metal Nanoparticles with TiO2 and Metal-Support Interaction in Photodeposition

作者：Ohyama Junya; Yamamoto Akira; Teramura Kentaro^*; Shishido Tetsuya; Tanaka Tsunehiro

来源：ACS Catalysis, 2011, 1(3): 187-192.

DOI：10.1021/cs100072k

• photodeposition
• Rh TiO2
• Pt-TiO2
• Au-TiO2
• M-TiO
• photoirradiation
• EM
• EDX
• XAFS
• XPS
• depth analysis

Rh, Pt, and Au metals photodeposited on TiO2 with an anatase phase (M-TiO2(p), M: Rh, Pt, Au) were studied using transmission electron microscopy (TEM), scanning transmission electron microscopy, energy dispersive X-ray (EDX) analysis, X-ray absorption fine structure ()LAPS) spectroscopy, X-ray photoelectron spectroscopy (XPS), and XPS depth profile analysis. The TEM images of Rh-TiO2-(p) and Pt TiO2(p) did not clearly show the grain boundary of metal particles, although the Rh and Pt species of Rh TiO2-(p),and Pt TiO2-(p) were observed by EDX analysis to show the metal particles 10-20 nm in size. These results suggest that the photodeposited Rh and Pt metal particles have a disorganized structure, which is also supported by extended XAFS spectral analysis. It is speculated that a strong metal support inter-action takes place in the case of Rh and Pt, resulting in the disorganized structure In the case of 4u, however, metal particles with a well organized and spherical structure were observed, indicating that Au does not strongly interact with TiO2. The XPS analyses revealed that the surface of metal particles of M-TiO2(p) received electrons from TiO2. The)(PS depth profile analysis suggests that the metal particles are modified with TiO2. TiO2-delta.generated by the photoirradiation of TiO2 can cause the modification and the disorganized structure of Rh and Pt metal particles.

• 出版日期2011-3