Experiments consisting of melting followed by thermal stabilization under a temperature gradient have been performed on Al-Ni peritectic alloys. A non-planar interface around the peritectic temperature has been observed. This is found to be induced by the primary Al3Ni2 phase dissolution above the equilibrium peritectic temperature T-P. A solute depleted zone in a distance above T-P and a solute enriched zone below T-P have been characterized. The dissolution perturbation is explained in light of the constitutional superheating driven by solute diffusion under a temperature gradient.