Macroporous poly (L-lactic acid)/chitosan nanofibrous scaffolds through cloud point thermally induced phase separation for enhanced bone regeneration

作者：Chen, Si; Zhao, Xiujuan; Du, Chang^*

来源：European Polymer Journal, 2018, 109: 303-316.

DOI：10.1016/j.eurpolymj.2018.10.003

• Poly (L-lactic acid)
• Chitosan
• Macroporous
• Thermal induced phase separation

A new method called cloud point thermally induced phase separation (CP-TIPS) was developed to prepare poly (L-lactic acid) (PLLA) scaffolds with macropores over 300 tins in PLLA/dioxane/H2O ternary system. The concentration of PLLA was 4% (w/v), and the solvent was dioxane with 14% of deionized water. By maintaining the clear solution of the ternary system near and above the cloud point for 2 h, followed by a large enough quenching depth ( - 80 degrees C), the crystallization of the alpha'-form crystal became privileged, and the microstructure of the pore wall was dominated with nanofibers. In contrast, conventional TIPS process resulted in scaffolds with similar pore size but platelet-like microstructure on the pore walls. The unique macroporous nanofibrous PLLA scaffold showed well elasticity and flexibility after swelling in 70% acetone. This property further enabled a facile "mechanical squeeze and intake" of high concentration viscous chitosan solution into the porous structure to modify the composite scaffolds. The compressive modulus of macroporous nanofibrous PLLA/CS scaffolds reached about 1 MPa. The hydrophilicity of the scaffold was greatly enhanced and the pH value remained stable in the first 3 weeks after degradation in vitro. The effect of chitosan concentration in the composite scaffolds on cell affinity and the osteogenic differentiation was evaluated. Finally, a critical-size rat calvarial bone defect model was used to evaluate the osteogenesis of the scaffolds in vivo and the composite scaffold with 3% chitosan significantly enhanced bone regeneration.

• 出版日期2018-12
• 单位华南理工大学