A comparison between different fouling-release elastomer coatings containing surface-active polymers

作者：Yasani B R; Martinelli E^*; Galli G; Glisenti A; Mieszkin S; Callow M E; Callow J A

来源：Biofouling, 2014, 30(4): 387-399.

DOI：10.1080/08927014.2013.878864

• mechanical properties
• films
• amphiphilic polymers
• fouling-release coatings
• antifouling coatings
• surface tension

Surface-active polymers derived from styrene monomers containing siloxane (S), fluoroalkyl (F) and/or ethoxylated (E) side chains were blended with an elastomer matrix, either poly(dimethyl siloxane) (PDMS) or poly(styrene-b-(ethylene-co-butylene)-b-styrene) (SEBS), and spray-coated on top of PDMS or SEBS preformed films. By contact angle and X-ray photoelectron spectroscopy measurements, it was found that the surface-active polymer preferentially populated the outermost layers of the coating, despite its low content in the blend. However, the self-segregation process and the response to the external environment strongly depended on both the chemistry of the polymer and the type of matrix used for the blend. Additionally, mechanical testing showed that the elastic modulus of SEBS-based coatings was one order of magnitude higher than that of the corresponding PDMS-based coatings. The coatings were subjected to laboratory bioassays with the marine alga Ulva linza. PDMS-based coatings had superior fouling-release properties compared to the SEBS-based coatings.

• 出版日期2014-4-21