New anhydrous proton exchange membranes based on fluoropolymers blend imidazolium poly (aromatic ether ketonejs for high temperature polymer electrolyte fuel cells

作者：Yang, Jingshuai^*; Wang, Yihan; Yang, Guohao; Zhan, Sifan

来源：International Journal of Hydrogen Energy, 2018, 43(17): 8464-8473.

DOI：10.1016/j.ijhydene.2018.03.128

• Blend
• Electrolyte membrane
• High temperature
• Fuel cell

The blend polymer membranes were synthesized from the methylimidazolium poly (aromatic ether ketone) (MeIm-PAEK) and fluoropolymers (PVDF and PVDF-HFP) with excellent thermal stability and improved dimensional stabilities for high-temperature polymer electrolyte fuel cells. The MeIm-PAEK exhibited good compatibility with PVDF or PVDF-HFP without phase separation. High phosphoric acid doping contents of the blend membranes were achieved at elevated temperatures with acceptable swellings. The acid doped blend membranes displayed lower dimensional swellings and higher mechanical strength compared to the MeIm-PAEK membrane, which allowed the blend membranes to obtain higher acid doping contents and proton conductivities. The MeIm-PAEK/10%PVDF membrane with a phosphoric acid doping content of 700 wt% showed a proton conductivity as high as 0.192 S cm(-1) at 180 degrees C under the non -humidified condition and a tensile strength of 4.3 MPa at room temperature.

• 出版日期2018-4-26
• 单位东北大学