Microstructural sintering evolution and sintering parameters optimization of the silica-doped Nd:YAG ceramics using the co-precipitated raw powder

作者：Ma Benyuan; Lu Tiecheng^*; Zhang Wei; Wei Nian; Lu Zhongwen; Chen Xingtao; Shi Yanli

来源：Journal of the European Ceramic Society, 2015, 35(8): 2403-2412.

DOI：10.1016/j.jeurceramsoc.2015.02.003

• Transparent ceramics
• Co-precipitation
• Liquid phase
• Sintering evolution
• Sintering schedule

Using the co-precipitated Nd:YAG raw powder, combined with 0.14 wt.% SiO2 as sintering aid, the green compacts were vacuum sintered from 1250 to 1750 degrees C to track the microstructural evolution during ceramic sintering process. The SEM results showed that a silicon-related liquid-phase sintering (1400-1550 degrees C) could greatly promote the densification process of ceramics with the ceramics at 1550 degrees C becoming translucent. Based on the evolution results, the parameters of sintering schedule, especially intermediate temperature holds and heating rates, were changed and optimized. The corresponding SEM morphologies and the influence mechanism were investigated. The results revealed that intermediate temperature holds (1250, 1450 and 1600 degrees C) and slower heating rates (1-5 degrees C/min) had a significant role in the pore elimination, the fine microstructure of ceramic and the promotion of ceramic transmittance. Using the optimized sintering schedule, a ceramic with fine microstructure could be obtained with a transmittance of 83.8% at 1064 nm.

• 出版日期2015-8
• 单位四川大学; 南阳师范学院; 核工业西南物理研究院