Direct Synthesis of Novel and Reactive Sulfide-modified Nano Iron through Nanoparticle Seeding for Improved Cadmium-Contaminated Water Treatment

作者：Su, Yiming; Adeleye, Adeyemi S.; Huang, Yuxiong; Zhou, Xuefei; Keller, Arturo A.^*; Zhang, Yalei^*

来源：Scientific Reports, 2016, 6(1): 24358.

DOI：10.1038/srep24358

• ZERO-VALENT IRON
• ZEROVALENT IRON
• WASTE-WATER
• AQUEOUS-SOLUTION
• NUCLEATION
• GROWTH
• PARTICLES
• REMOVAL
• NZVI
• DECHLORINATION

Magnetic sulfide-modified nanoscale zerovalent iron (S-nZVI) is of great technical and scientific interest because of its promising application in groundwater remediation, although its synthesis is still a challenge. We develop a new nanoparticle seeding method to obtain a novel and reactive nanohybrid, which contains an Fe(0) core covered by a highly sulfidized layer under high extent of sulfidation. Syntheses monitoring experiments show that seeding accelerates the reduction rate from Fe2+ to Fe-0 by 19%. X-ray adsorption near edge structure (XANES) spectroscopy and extended X-ray absorption fine structure analyses demonstrate the hexahedral Fe-Fe bond (2.45 and 2.83 angstrom) formation through breaking down of the 1.99 angstrom Fe-O bond both in crystalline and amorphous iron oxide. The XANES analysis also shows 24.2% (wt%) of FeS with bond length of 2.4 angstrom in final nanohybrid. Both X-ray diffraction and Mossbauer analyses further confirm that increased nanoparticle seeding results in formation of more Fe-0 crystals. Nano-SiO2 seeding brings down the size of single Fe-0 grain from 32.4 nm to 18.7 nm, enhances final Fe-0 content from 5.9% to 55.6%, and increases magnetization from 4.7 to 65.5 emu/g. The synthesized nanohybrid has high cadmium removal capacity and holds promising prospects for treatment of metal-contaminated water.

• 出版日期2016-4-20
• 单位同济大学