Magnetic irreversibility of the Fe antidot arrays film by depositing on the porous alumina templates

作者：Jiang, Changjun^*; Wei, Wenwen; Liu, Qingfang; Guo, Dangwei; Xue, Desheng

来源：Applied Surface Science, 2012, 258(8): 3723-3725.

DOI：10.1016/j.apsusc.2011.12.013

• Magnetic irreversibility
• Low-temperature
• Antidot arrays
• Fe

An Fe layer was sputter-deposited onto porous alumina templates and Kapton respectively. Fe layer on the porous alumina templates formed an antidot arrays nanostructure, while Fe layer on the Kapton substrate formed a continuous film. Scanning electron microscopy and grazing incidence X-ray diffraction were employed to characterize the morphology and crystal structure of the Fe antidot arrays and continuous film, respectively. The temperature dependence of magnetic properties was shown in the temperature range 2-300 K. The irreversibility of the magnetization of Fe antidot arrays film, as measured in zero-field cooling (ZFC) and field cooling (FC) states, was attributed to the pinning effect of the holes.

• 出版日期2012-2-1
• 单位兰州大学